mariss, std thickness are .025 .032, .040, .050, .063, .080, .090, .125
availability from distributors varies by alloy, for best strength to
thickness
ratio, 6061-t6 can't be beat, for best cost/strength ratio 5052-H32, I use
alot
of 3003-H14 because it's easy to bend with a brake, though machineability
isn't
nearly as good as 5052.
Erie Patsellis
Shelbyville Design & signworks
217-774-4444
erie@... <mailto:erie@...>
Visit our website at: www.shelbyvilledesign.com
-----Original Message-----
From: Mariss Freimanis <mariss92705@...>
[mailto:mariss92705@...]
Sent: Tuesday, February 11, 2003 7:54 PM
To: CAD_CAM_EDM_DRO@yahoogroups.com
Subject: [CAD_CAM_EDM_DRO] Quick OT question
Hi,
I need to ask the sheet metal gurus on this list what are the most
common standard aluminum thicknesses between 0.05" and 0.125". I have
to design up an enclosure for the G2002 and I need to know what I can
use. Thanks.
Mariss
Addresses:
FAQ: http://www.ktmarketing.com/faq.html
FILES: http://groups.yahoo.com/group/CAD_CAM_EDM_DRO/files/
Post Messages: CAD_CAM_EDM_DRO@yahoogroups.com
Subscribe: CAD_CAM_EDM_DRO-subscribe@yahoogroups.com
Unsubscribe: CAD_CAM_EDM_DRO-unsubscribe@yahoogroups.com
List owner: CAD_CAM_EDM_DRO-owner@yahoogroups.com, wanliker@...,
timg@...
Moderator: pentam@... indigo_red@... [Moderators]
URL to this group: http://groups.yahoo.com/group/CAD_CAM_EDM_DRO
OFF Topic POSTS: General Machining
If you wish to post on unlimited OT subjects goto:
aol://5863:126/rec.crafts.metalworking or go thru Google.com to reach it if
you have trouble.
http://www.metalworking.com/news_servers.html
http://groups.yahoo.com/group/jobshophomeshop I consider this to be a
sister site to the CCED group, as many of the same members are there, for OT
subjects, that are not allowed on the CCED list.
NOTICE: ALL POSTINGS TO THIS GROUP BECOME PUBLIC DOMAIN BY POSTING THEM.
DON'T POST IF YOU CAN NOT ACCEPT THIS.....NO EXCEPTIONS........
bill
List Mom
List Owner
Your use of Yahoo! Groups is subject to http://docs.yahoo.com/info/terms/
availability from distributors varies by alloy, for best strength to
thickness
ratio, 6061-t6 can't be beat, for best cost/strength ratio 5052-H32, I use
alot
of 3003-H14 because it's easy to bend with a brake, though machineability
isn't
nearly as good as 5052.
Erie Patsellis
Shelbyville Design & signworks
217-774-4444
erie@... <mailto:erie@...>
Visit our website at: www.shelbyvilledesign.com
-----Original Message-----
From: Mariss Freimanis <mariss92705@...>
[mailto:mariss92705@...]
Sent: Tuesday, February 11, 2003 7:54 PM
To: CAD_CAM_EDM_DRO@yahoogroups.com
Subject: [CAD_CAM_EDM_DRO] Quick OT question
Hi,
I need to ask the sheet metal gurus on this list what are the most
common standard aluminum thicknesses between 0.05" and 0.125". I have
to design up an enclosure for the G2002 and I need to know what I can
use. Thanks.
Mariss
Addresses:
FAQ: http://www.ktmarketing.com/faq.html
FILES: http://groups.yahoo.com/group/CAD_CAM_EDM_DRO/files/
Post Messages: CAD_CAM_EDM_DRO@yahoogroups.com
Subscribe: CAD_CAM_EDM_DRO-subscribe@yahoogroups.com
Unsubscribe: CAD_CAM_EDM_DRO-unsubscribe@yahoogroups.com
List owner: CAD_CAM_EDM_DRO-owner@yahoogroups.com, wanliker@...,
timg@...
Moderator: pentam@... indigo_red@... [Moderators]
URL to this group: http://groups.yahoo.com/group/CAD_CAM_EDM_DRO
OFF Topic POSTS: General Machining
If you wish to post on unlimited OT subjects goto:
aol://5863:126/rec.crafts.metalworking or go thru Google.com to reach it if
you have trouble.
http://www.metalworking.com/news_servers.html
http://groups.yahoo.com/group/jobshophomeshop I consider this to be a
sister site to the CCED group, as many of the same members are there, for OT
subjects, that are not allowed on the CCED list.
NOTICE: ALL POSTINGS TO THIS GROUP BECOME PUBLIC DOMAIN BY POSTING THEM.
DON'T POST IF YOU CAN NOT ACCEPT THIS.....NO EXCEPTIONS........
bill
List Mom
List Owner
Your use of Yahoo! Groups is subject to http://docs.yahoo.com/info/terms/
Discussion Thread
Mariss Freimanis <mariss92705@y...
2003-02-11 17:54:23 UTC
Quick OT question
EdFanta
2003-02-11 18:07:33 UTC
Re: [CAD_CAM_EDM_DRO] Quick OT question
Mariss Freimanis <mariss92705@y...
2003-02-11 18:14:24 UTC
Re: Quick OT question
turbulatordude <davemucha@j...
2003-02-11 18:59:30 UTC
Re: Quick OT question
RichD
2003-02-11 19:56:07 UTC
Re: [CAD_CAM_EDM_DRO] Quick OT question
Erie Patsellis
2003-02-12 08:02:06 UTC
RE: [CAD_CAM_EDM_DRO] Quick OT question
Jon Elson
2003-02-12 10:15:36 UTC
Re: [CAD_CAM_EDM_DRO] Quick OT question