Re: [CAD_CAM_EDM_DRO] Milling HSS
Posted by
ptengin@a...
on 2000-09-09 13:06:46 UTC
In a message dated 9/8/00 11:40:51 AM Hawaiian Standard Time,
dengvall@... writes:
<< Darrell wrote:It should be annealed first.
Ouch: dT/dt for annealing M2 is 20 degrees F/hr. from 1600 down to black
(maybe 1000-1100). Not the easiest thing to do.
Grinding sounds good to me.
Dave >>
Pragrammable ovens can do the trick. I'd hate to sit there on fire watch that
many hours though....
Peter
THRD, Inc.
dengvall@... writes:
<< Darrell wrote:It should be annealed first.
Ouch: dT/dt for annealing M2 is 20 degrees F/hr. from 1600 down to black
(maybe 1000-1100). Not the easiest thing to do.
Grinding sounds good to me.
Dave >>
Pragrammable ovens can do the trick. I'd hate to sit there on fire watch that
many hours though....
Peter
THRD, Inc.
Discussion Thread
Darrell
2000-09-08 14:09:02 UTC
Re: [CAD_CAM_EDM_DRO] Milling HSS
James Owens
2000-09-08 14:34:17 UTC
Re: [CAD_CAM_EDM_DRO] Milling HSS
dave engvall
2000-09-08 14:38:10 UTC
Re: [CAD_CAM_EDM_DRO] Milling HSS
Darrell
2000-09-08 14:40:30 UTC
Re: [CAD_CAM_EDM_DRO] Milling HSS
Jon Elson
2000-09-08 15:20:43 UTC
Re: [CAD_CAM_EDM_DRO] Milling HSS
Paul Corner
2000-09-08 18:23:20 UTC
Re: [CAD_CAM_EDM_DRO] Milling HSS
ptengin@a...
2000-09-09 13:06:46 UTC
Re: [CAD_CAM_EDM_DRO] Milling HSS
Chris Paine
2000-09-12 14:42:03 UTC
Re: [CAD_CAM_EDM_DRO] Milling HSS
dave engvall
2000-09-13 20:01:28 UTC
Re: [CAD_CAM_EDM_DRO] Milling HSS