Re: [CAD_CAM_EDM_DRO] Threads on a ball screw........

Annealing the end of the ballscrew first is the obvious answer.

I think someone posted this before, but here's a video on the process;


http://www.youtube.com/watch?v=dzIsR4Mg158


Roland

On 26 February 2010 00:15, david@fignoggle - IMAP <david@...>wrote:

>
> it's the interrupted cuts that also create a bit of a problem. again,
> with proper insert tooling or lots of hss grinding, the material is
> easier to cut after the threads are removed. we use a ccmt 21.51
> style/size insert and the smaller radius seems to cut better than some
> of the larger triangle/trigon inserts we've tried.
>
> to get a nice, polished finish on the journals, you can leave a thou or
> so and spin up your lathe and use sandpaper belts of a desired width.
> usually, after 400 grit, your finish will be pretty nice.
>
> hope this helps!
>
> --
> --
> Spindle Lock for your Rong-Fu 45, Lathemaster, Sieg X3 <
> http://www.spindle-lock.com>
> CNC, Plans/Kits, 8x12 Lathe, Mini-Mill, How-Tos <http://www.fignoggle.com>
> Sieg X3/Super X3 Mill Information, HF/Enco Coupons <http://www.superx3.com
> >
>
>
>
> Steve Blackmore wrote:
> >
> > On Tue, 23 Feb 2010 16:33:39 -0500, you wrote:
> >
> > >What is this "sleeve goop" you speak of, something better than
> > threadlocker?
> > >
> > >Those ballscrews ARE nearly impossible to cut down or thread, makes a
> > good case for making yourself an inexpensive toolpost grinder. You
> > just have to cover your entire machine with plastic so you don't get
> > the grinding mess into your ways.
> >
> > I've turned and threaded ballscrews without any problems? They are only
> > usually 4140 or 4150 alloy steel or 1050 Carbon steel. You need to take
> > deep roughing cuts to get through the surface hardness with Carbide
> > insert tooling. Something like Iscar IC3028 inserts are good for that.
> > Once through the surface they are no trouble at all with normal insert
> > tooling.
> >
> > Steve Blackmore
> > --
> >
> >
> >
> > --
> > This message has been scanned for viruses and
> > dangerous content by *MailScanner* <http://www.mailscanner.info/>, and
> is
> > believed to be clean.
>
>
>
> ------------------------------------
>
> Addresses:
> FAQ: http://www.ktmarketing.com/faq.html
> FILES: http://groups.yahoo.com/group/CAD_CAM_EDM_DRO/files/
> Post Messages: CAD_CAM_EDM_DRO@yahoogroups.com
>
> Subscribe: CAD_CAM_EDM_DRO-subscribe@yahoogroups.com
> Unsubscribe: CAD_CAM_EDM_DRO-unsubscribe@yahoogroups.com
> List owner: CAD_CAM_EDM_DRO-owner@yahoogroups.com, wanliker@...,
> timg@...
> Moderator: pentam@... indigo_red@... davemucha@... [Moderators]
> URL to this group: http://groups.yahoo.com/group/CAD_CAM_EDM_DRO
>
> OFF Topic POSTS: General Machining
> If you wish to post on unlimited OT subjects goto:
> aol://5863:126/rec.crafts.metalworking or go thru Google.com to reach it if
> you have trouble.
> http://www.metalworking.com/news_servers.html
>
> http://groups.yahoo.com/group/jobshophomeshop I consider this to be a
> sister site to the CCED group, as many of the same members are there, for OT
> subjects, that are not allowed on the CCED list.
>
> NOTICE: ALL POSTINGS TO THIS GROUP BECOME PUBLIC DOMAIN BY POSTING THEM.
> DON'T POST IF YOU CAN NOT ACCEPT THIS.....NO EXCEPTIONS........
> bill
> List Mom
> List Owner
>
> Yahoo! Groups Links
>
>
>
>


[Non-text portions of this message have been removed]