Re: [CAD_CAM_EDM_DRO] cast iron
Posted by
dave engvall
on 2001-02-08 09:56:38 UTC
Carlos Guillermo wrote:
A. proper composition of the iron........ I think implies meehanite
B. "Stability of iron depends mostly on slow, uniform cooling in the mold after casting."
Further down the page the author talks about a Moore jig grinder that had been thru a fire. Melted the aluminum guards. After a
solvent cleanup. "there was virtually no deviation from the original factory calibration".
HTH
Dave
p.s. I have heard about shops leaving there casting out in the weather for a few years to age before using them. I suspect Century
(lathes) did that from the mess behind their shop.
> List -In Moore's "Foundations of Mechanical Accuracy" pg. 17.
>
> I've got some questions about some castings I'll be having made soon. There
> was recently some mention of aging the cast iron before machining, and I'm
> wondering, how long one should let it age?
>
> Carlos Guillermo
> VERVE Engineering & Design
>
A. proper composition of the iron........ I think implies meehanite
B. "Stability of iron depends mostly on slow, uniform cooling in the mold after casting."
Further down the page the author talks about a Moore jig grinder that had been thru a fire. Melted the aluminum guards. After a
solvent cleanup. "there was virtually no deviation from the original factory calibration".
HTH
Dave
p.s. I have heard about shops leaving there casting out in the weather for a few years to age before using them. I suspect Century
(lathes) did that from the mess behind their shop.
Discussion Thread
Carlos Guillermo
2001-02-08 09:35:50 UTC
cast iron
dave engvall
2001-02-08 09:56:38 UTC
Re: [CAD_CAM_EDM_DRO] cast iron
Joe Vicars
2001-02-08 10:36:33 UTC
Re: [CAD_CAM_EDM_DRO] cast iron
ballendo@y...
2001-02-08 11:08:19 UTC
Re: [CAD_CAM_EDM_DRO] cast iron
Dan Mauch
2001-02-08 11:09:08 UTC
Re: [CAD_CAM_EDM_DRO] cast iron
Carlos Guillermo
2001-02-08 11:54:52 UTC
RE: [CAD_CAM_EDM_DRO] cast iron
ballendo@y...
2001-02-08 12:02:34 UTC
RE: [CAD_CAM_EDM_DRO] cast iron
James Owens
2001-02-08 12:57:13 UTC
Re: [CAD_CAM_EDM_DRO] cast iron
Alan Marconett KM6VV
2001-02-08 13:10:10 UTC
Re: [CAD_CAM_EDM_DRO] cast iron
ballendo@y...
2001-02-08 13:56:34 UTC
Re: cast iron
Carlos Guillermo
2001-02-08 14:08:17 UTC
RE: [CAD_CAM_EDM_DRO] cast iron
dave.schultz@s...
2001-02-08 15:37:07 UTC
Re: cast iron
ballendo@y...
2001-02-08 15:46:22 UTC
re:Re: cast iron (stress relieving)
dave.schultz@s...
2001-02-08 16:04:52 UTC
re:Re: cast iron (stress relieving)
dave engvall
2001-02-08 16:43:51 UTC
Re: [CAD_CAM_EDM_DRO] cast iron
Carlos Guillermo
2001-02-08 17:58:10 UTC
RE: [CAD_CAM_EDM_DRO] cast iron
Sven Peter, TAD S.A.
2001-02-08 18:40:36 UTC
Re: [CAD_CAM_EDM_DRO] cast iron
davemucha@j...
2001-02-08 20:19:57 UTC
re:Re: cast iron (stress relieving)
davemucha@j...
2001-02-08 20:23:46 UTC
re:Re: cast iron (stress relieving)
Smoke
2001-02-08 20:49:54 UTC
Re: [CAD_CAM_EDM_DRO] cast iron
Jay Hayes
2001-02-08 22:25:01 UTC
Re: [CAD_CAM_EDM_DRO] cast iron
ballendo@y...
2001-02-09 03:53:54 UTC
Re: cast iron
James Owens
2001-02-09 04:15:01 UTC
Re: [CAD_CAM_EDM_DRO] Re: cast iron
Carlos Guillermo
2001-02-09 06:44:34 UTC
cast iron
ballendo@y...
2001-02-09 12:22:14 UTC
RE:re:Re: cast iron
Smoke
2001-02-09 13:08:19 UTC
Re: [CAD_CAM_EDM_DRO] cast iron
machines@n...
2001-02-09 16:03:26 UTC
Re: cast iron
Smoke
2001-02-10 08:28:33 UTC
Re: [CAD_CAM_EDM_DRO] Re: cast iron
Smoke
2001-02-10 08:37:34 UTC
Re: [CAD_CAM_EDM_DRO] cast iron
dave engvall
2001-02-10 10:04:07 UTC
Re: [CAD_CAM_EDM_DRO] Re: cast iron
davemucha@j...
2001-02-10 14:09:17 UTC
Re: cast iron
James Owens
2001-02-10 14:43:58 UTC
Re: [CAD_CAM_EDM_DRO] RE:re:Re: cast iron
davemucha@j...
2001-02-10 18:08:39 UTC
RE:re:Re: cast iron